铜离子交换改性的沸石催化剂上甲烷的非氧芳构化

已有研究表明，ＭｏＯ３／ＨＺＳＭ５是甲烷非氧芳构化的优良催化剂，在９７３Ｋ下甲烷转化率达６％～８％，苯选择性高于８０％，这为非氧气氛下甲烷的芳构化反应展示了非常诱人的前景［１～１２］．但是，该催化剂的活性和稳定性尚有待进一步提高，目前已有使用Ｐｔ，...     

分子筛模型中非骨架离子位置的研究

从理论上研究了非骨架阳离子可能的分布位置．计算了分子筛晶体基本结构单元在整个空间的静电势分布，找出空间中静电势的各个极小点．在静电势最低点逐个放置钠离子，优化，重新计算模型分子筛的电势分布．研究了阳离子放置过程中静电势变化的趋势．     

等离子体辅助合成分子筛膜及其催化性能的研究

首次将等离子体技术应用于分子筛膜的制备，研究了以微波等离子体处理基材表面分子筛膜前驱体辅助水热反应合成支撑β型分子筛膜．利用XRD、SEM、XPS、BET、TPD表征了分子筛膜的物相、形貌、孔结构、表面元素组成和表面酸性，并通过甲醇与异丁烯液相反应体系实验考察了分子筛膜的催化性能．结果表明，等离子体处理能有效改善分子筛膜前驱体在基材表面的分散状况，减小了分子筛膜晶体的尺度，使晶体大小均匀，形成的膜致密、牢固．与采用常规方法合成的分子筛膜相比，等离子体辅助合成的分子筛膜对甲醇与异丁烯的反应有更好的催化活件．     

以偏钛酸为原料常压水热法合成纳米钛酸锶

以廉价的工业级偏钛酸和氯化锶为原料,用常压水热法于100℃反应6 h一步合成了纳米钛酸锶。当n(SrC l2)∶n(H3TiO3)=1.0∶1.1,pH=12时,所得钛酸锶的n(Ti)∶n(Sr)=1.02∶1.00。纳米钛酸锶经IR,XRD和TEM表征。结果显示,钛酸锶为球形粒子,属立方晶系(a=3.9200);一次粒径平均值为22 nm,粒径分布为20 nm~40 nm,无明显团聚。     

MoCo/Y, MoNi/Y氮化物催化剂的结构和CH4+CO2重整反应性能

采用氨气还原法制备了NaY分子筛负载的MoCo/Y、MoNi／Y双组氮化物催化剂，用XRD和EXAFS方法征了样品的结构，并测定了其在CH4＋CO2重整反应中的活性，在氧化态时，MoCo/Y样品中主要存在CoMoO4和Co3O4两种物相，Mo的配位状态接近于CoMoO4，而Co的配位状态更接近于Co3O4，MoNi／Y样品中主要有NiMoO4和NiO两种物相，Mo的配位状态接近于MiMoO4，而Ni的配位状态可能是NiMoO4和NiO两种化合物中Ni配位状态的平均效果，Ni-Mo之间的朴素作用似乎比Co-Mo相对较强，在氮化态时，两种样品中Mo的配位状态较为相似，但即不同于MoO3，也不同于单组分γ－Mo2N.Co和Ni的配位状态都不同于各在氧化态下的状态，且都在相同的位置出现一个新强峰，这似乎表明MoCo和MoNi生成了结构相似的氮化物，在CH4＋CO2重整反应中，氮化态MoCO/Y和MoNi/Y的活性大大超过非负载单组分γ－Mo2N催化剂，其中MoNi/Y的活性相对更好一些，且活性随Ni含量增加而提高。     

纳米镍-铁合金/膨胀石墨复合材料的制备、表征及其电磁屏蔽性能

The composites with nano-particles of Ni-Fe alloys dispersed on the nano-layers of expanded graphite (EG) were prepared by the impregnation of EG with ethanol solutions of nickel and iron acetates， followed by drying and reduction in H₂. The square nano-particles of Ni-Fe alloys with particle sizes of mainly 20～40 nm were found to be well spread on the layers of EG. The alloy nano-particles exhibited high shielding effectiveness (SE) for electromagnetic radiations at low frequencies due to their high magnetic conductivity. Since EG is electronically conductive and displayed high SE at high frequencies， the composites exhibited good SE at wide range of frequencies. The electric and magnetic conductivities of the composites could be monitored through regulating the loadings of alloy nano-particles on EG， and it was found that the composites with 20%～40% of the alloys exhibited good SE. Specifically， the composite 27%Ni-3%Fe-EG showed the excellent SE from 66 to 110 dB at the frequencies from 300 kHz to 1.5 GHz.     

SXI route to mesostructured materials from Fau and Beta zeolite precursors: A comparative study of their assembly behaviors in extremely acidic media

Mesoporous molecular sieves were synthesized from Beta and Fau zeolite precursors through S⁺X⁻I⁺ route under extremely acidic conditions in parallel (designated as M_Beta and M_Fau, respectively). The textural properties of M_Fau were different from its M_Beta counterpart but resembled normal MCM-41 silica from TEOS. Al content in M_Beta was almost equivalent to that in the initial Beta zeolite precursors, whereas only trace Al species was present in M_Fau from elemental analysis results. The hydrothermal stability of M_Beta after post-synthesis ammonia treatment was considerably improved compared with normal MCM-41 aluminosilicates, whereas the M_Fau after the same procedure was as unstable as normal MCM-41 silica. Thus, the assembly behaviors of Beta and Fau zeolite precursors were comparatively studied based on these results. The microstructure of Fau zeolite precursors were degraded by the extremely acidic condition, and Al species was dissolved into the synthesis mixture. However, Beta zeolite precursors survived the chemical attack of extremely acidic media and were incorporated into mesostructured framework as primary building units.     

Structural evolution of calcium-exchanged (NH4)2SiF6-dealuminated Y zeolite after various chemical treatments

The structural evolution of Y zeolite (Si/Al 2.17) weakly dealuminated by hexafluorosilicate (Si/Al 3.13), denoted Y_D, and exchanged with calcium (CaY_D), has been studied after acid–base treatments at 80 °C close to the cation exchange conditions. The stability of the samples was followed by X-ray diffraction and solid-state NMR of ²⁹Si and ²⁷Al; Y_D zeolite was completely destroyed by treatment with acid pH 2.5 and suffered serious degradation on treatment with alkali at pH 11.8. The introduction of calcium improved the stability of the zeolite in acid and base. In acid CaY_D was not destroyed until pH 1. At pH 2, silicon and aluminium were extracted and an amorphous phase was formed. Base treatment at pH 13 did not affect the calcium-exchanged zeolite.     

高硅ZSM—5沸石填充硅橡胶膜的醇—水渗透蒸发分离性质

高硅ZSM－5沸石填充疏水性硅橡胶蓦地低浓度醇－水体度醇－水体的渗透蒸发性质的研究有明，提高沸石硅铝比，增加填充量以及进行酸处理皆有利于改善膜对醇－水的分离系数和通量。料液的成，浓度以及温度对膜的分离性质也有显著影响。     

杂原子Y分子筛的二次合成及其吸附脱硫性能

采用液-固相同晶取代反应制备了骨架含Ga的Y型分子筛, 并对其吸附脱硫性能进行了研究. 在室温, 空速为7 h−1的条件下, 镓化Y型分子筛([Ga]AlY)处理噻吩、四氢噻吩、4,6-二甲基二苯并噻吩(4,6-DMDBT)正壬烷溶液(硫含量500 μg•g−1), 每克吸附剂吸附硫的量分别为7.7、17.4、14.5 mg. 采用密度泛函理论(DFT)中的广义梯度近似方法(GGA)计算各分子中硫原子上的电荷数, 噻吩中硫原子的电荷数为−0.159, 而4,6-DMDBT和四氢噻吩分别为−0.214、0.298. 四氢噻吩和4, 6-DMDBT中硫原子上的电子密度大于噻吩中硫原子上的电子密度, 这就使得四氢噻吩和4,6-DMDBT中的硫原子与吸附位间的作用会远大于噻吩中的硫原子与吸附位间的作用, 吸附容量必然会大很多. 采用[Ga]AlY处理抚顺石油二厂的催化裂化汽油(硫含量：299 μg•g−1), 每克吸附剂处理2.1 mL汽油时, 处理后汽油的硫含量为54.8 μg•g−1, 说明[Ga]AlY对汽油脱硫有一定的效果.